Synthesis and Electrochemical Properties of Nano WO3/C Composite for Lithium-Ion Batteries

The WO3/C nano-belts composite was prepared through a hydrothermal synthesis method by using (NH4)10H2(W2O7)6, H2C2O4·2H2O and different proportions of glucose as reactants. The WO3/C samples were characterized by X-ray diffraction and scanning electron microscopy. The electrochemical properties of the samples were investigated. The results show that the morphology of the samples was nano-belts with a width of about 5~15 nm structure. The electrochemcial testing showed that the WO3/C nano-belts with the 20 wt.% of the raw material weight of glucose exhibited good lithium storage properties, with a high reversible capability (700 mAh/g at current density of 50 mA/g) and stable lithium-ion insertion/de-insertion reversibility. Besides, the WO3/C nano-belts bahaved rate capacity and outstanding cycle performance. It is a promising anode material for lithium ion battery application.