In present study electrochemical deposition technology was used to modify the activated carbon (AC) cathode with hydrangea-like Cu2O and notrogen simultaneously, and the performance was improved greatly. The maximum power density was 1613±25 mW m-2, 84% and 62% more than controls repsectively. The electrochemical performances of cathodes were evaluated by Linear sweep voltammetry, exchange current density (i0) and Electrochemical impedance spectroscopy. Hydrangea-like mophology provided more active sites and channels for electrons of oxygen reduction reaction. X-ray XRD, FTIR and XPS results the existence of oxygen vacancy, crystal defects, acidic functional groups and hydrophilic functional groups, and C-N bond, especially pyridine, pyrrole and quaternary N, played a significant catalytic role in oxygen reduction reaction. Electrodeposition is a promising way to modifi AC cathode with metal and nitrogen at the same time.