Three kinds of three-dimensional (3D) Cu_xO catalysts were prepared to modify activated carbon air-cathode using a facile electrochemical method with addition of surfactants. The maximum power density of MFC using SC-Cu air cathode (added sodium citrate into the electrolyte solution in eletrodeposition process) was 1550±47 mW m^-2, almost 77% higher than AC cathode. Specifically, the charge transfer resistance significantly decreased by 89% from 9.3980 Ω to 1.0640 Ω compared to the control. Lumphy and mutually embedded filmy sheet structure were observed in SEM, which provided sufficient active sites for oxygen adsorption and diffusion. In XRD and TEM result, Cu_xO with mixed facets showed special structure which had a better performance. Crystallization condition of electrodeposited materials played a significant role in their nature electrochemical properties, morphology controlled by surfactant of CuxO exhibited high properties on the air-cathode MFC.